dc.creatorMarinho, Cleidiney Corrêa-
dc.creator.Latteshttp://lattes.cnpq.br/7718070539586772por
dc.contributor.advisor1Macedo Neto, José Costa de-
dc.contributor.advisor1Latteshttp://lattes.cnpq.br/7868540287547126por
dc.contributor.referee1Cruz Neto, Rubelmar Maia de Azevedo-
dc.contributor.referee1Latteshttp://lattes.cnpq.br/6313312439770632por
dc.contributor.referee2Lopes, Arlindo Pires-
dc.contributor.referee2Latteshttp://lattes.cnpq.br/4442264741576143por
dc.date.issued2020-03-12-
dc.identifier.citationMARINHO, Cleidiney Corrêa. Influência da preparação de juntas soldadas pelo Processo Arame Tubular na microestrutura e resistência mecânica do Aço Naval ASTM A131-A. 2020. 113 f. Dissertação (Mestrado em Ciência e Engenharia de Materiais) - Universidade Federal do Amazonas, Manaus, 2020.por
dc.identifier.urihttps://tede.ufam.edu.br/handle/tede/8278-
dc.description.resumoA goivagem na raiz é um processo que ocorre durante a soldagem para soldas dupla e é definida como sendo a remoção do metal de solda e metal base da raiz da primeira solda de uma junta soldada para garantir que não haja penetração inadequada da junta ou fusão incompleta entre as soldas e metal base, onde ambos resultam em pontos de tensão, e as rachaduras que podem iniciar e propagar-se a medida que cordões de solda são depositados. O objetivo desse estudo é analisar as microestruturas e propriedades mecânicas da junta soldada do aço ASTM A131-A, resultante da soldagem com arame tubular e goivagem por esmerilhamento da raiz. Microscopia óptica e eletrônica com espectrômetro de raio-x de energia dispersiva, foram utilizados para avaliar a microestrutura e inclusões, o ensaio de tração e nanoindentação foram usados para avaliar a resistência mecânica em todo o cordão de solda. Resultados mostraram que a profundidade da goivagem pode efetivamente reduzir a resistência mecânica do aço ASTM A131-A. A junta soldada com goivagem de 5,0 mm de profundidade exibiu uma redução na resistência mais proeminente do que a junta soldada com goivagem de 1,5 mm de profundidade, que, por sua vez, a goivagem com 1,5 mm de profundidade teve uma redução no tempo de fabricação de 28,27 % para uma chapa de 1300 mm de comprimento com 9,5 mm de espessura.por
dc.description.abstractBack gouging is a process that occurs during welding for double welds and is defined as the removal of the weld metal and base metal from the first weld of a welded joint to ensure that there is no inadequate joint penetration or incomplete fusion between welds and metal base, where both result in stress points, and the cracks that can start and propagate as weld beads are deposited. The objective of this study is to analyze the microstructures and mechanical properties of the welded joint of ASTM A131-A steel, resulting from flux cored arc welding and back gouging by grinding. Optical and electronic microscopy with x-ray spectrometer of dispersive energy, were used to evaluate the microstructure and inclusions, the tensile test and nanoindentation were used to evaluate the mechanical resistance in the entire weld bead. Results showed that the depth of gouging can effectively reduce the mechanical strength of ASTM A131-A steel. The 5.0 mm gouged welded joint exhibited a more prominent reduction in strength than the 1.5 mm gouged welded joint, which, in turn, the 1.5 mm deep gouge had a reduction in manufacturing time of 28.27% for a 1300 mm long plate with 9.5 mm thickness.eng
dc.description.sponsorshipFundação de Amparo à pesquisa do Estado do Amazonas - FAPEAMpor
dc.formatapplication/pdf*
dc.thumbnail.urlhttps://tede.ufam.edu.br//retrieve/46169/Disserta%c3%a7%c3%a3o_CleidineyMarinho_PPGCEM.pdf.jpg*
dc.languageporpor
dc.publisherUniversidade Federal do Amazonaspor
dc.publisher.departmentFaculdade de Tecnologiapor
dc.publisher.countryBrasilpor
dc.publisher.initialsUFAMpor
dc.publisher.programPrograma de Pós-graduação em Ciência e Engenharia de Materiaispor
dc.rightsAcesso Abertopor
dc.rights.urihttp://creativecommons.org/licenses/by/4.0/-
dc.subjectSoldagempor
dc.subjectCordão de soldapor
dc.subjectEspectrômetro de raio-xpor
dc.subjectNanoindentaçãopor
dc.subjectResistência mecânicapor
dc.subject.cnpqENGENHARIASpor
dc.titleInfluência da preparação de juntas soldadas pelo Processo Arame Tubular na microestrutura e resistência mecânica do Aço Naval ASTM A131-Apor
dc.typeDissertaçãopor
dc.contributor.advisor1orcidhttps://orcid.org/0000-0003-1155-0027por
dc.contributor.referee1orcidhttps://orcid.org/0000-0002-1408-5290por
dc.subject.userGoivagem na raizpor
dc.subject.userPenetração inadequadapor
dc.subject.userFusão incompletapor
dc.subject.userSoldagem com arame tubularpor
dc.subject.userAstm a131-apor
Appears in Collections:Mestrado em Ciência e Engenharia de Materiais

Files in This Item:
File Description SizeFormat 
Dissertação_CleidineyMarinho_PPGCEM.pdfDissertação_CleidineyMarinho_PPGCEM6.06 MBAdobe PDFThumbnail

Download/Open Preview


This item is licensed under a Creative Commons License Creative Commons