???metadata.dc.type???: Dissertação
Title: Estudos das propriedades físicas e mecânicas de placas cimentícias reforçadas com fibras longas de malva
???metadata.dc.creator???: Aguiar, Alcineia Silva de 
???metadata.dc.contributor.advisor1???: Vasconcelos, Raimundo Pereira de
???metadata.dc.contributor.referee1???: Melo Filho, João de Almeida
???metadata.dc.contributor.referee2???: Savastano Júnior, Holmer
???metadata.dc.description.resumo???: Com o objetivo de se obter vantagens técnicas, econômicas e ambientais, esta pesquisa desenvolveu um estudo da produção de placas cimentícias reforçadas com fibras longas de malva e avaliou o seu comportamento físico e mecânico. A motivação para o trabalho com esta fibra se deve a sua oferta em larga escala, baixo custo e resultados já satisfatórios em outras pesquisas, sendo estas preparadas, tratadas e caracterizadas. E para garantir a não deterioração destas fibras, fez-se o uso de resíduo cerâmico moído, em substituição de parte do cimento na matriz, produzindo uma pasta com baixo teor de hidróxido de cálcio livre, contribuindo para a proteção da fibra. Além disso, para reduzir a absorção de água e a consequente diminuição da variação dimensional da fibra, usou-se também o tratamento de hornificação e impermeabilização a base de verniz. Na produção deste compósito foi utilizado aditivo superplastificante, areia média, cimento Portland CP II 32-F e água. Com esses materiais foram produzidas placas com o uso de fôrmas acrílicas de dimensões de 40x40x1cm. Para a análise das propriedades mecânicas dessas placas foi necessário à realização dos ensaios de tração direta, flexão em quatro pontos e flexão em três pontos. Dos resultados obtidos, pode-se concluir que o compósito que apresentou os melhores resultados em termos das características físicas, por meio do ensaio de termogravimetria e caracterização das fibras, e mecânicas, por meio dos ensaios de tração e flexão, foi aquele produzido com fibras de malva hornificadas e impermeabilizadas com verniz e a substituição de 30% do cimento Portland pelo resíduo cerâmico, o qual apresentou módulo de elasticidade de 22,3 GPa, resistência à tração de 23 MPa e Módulo de ruptura de 38,6 MPa.
Abstract: In order to obtain technical, economic and environmental benefits, this research developed a study of the production of cement plates reinforced with long fibers of malva and assessed their physical and mechanical behavior. The motivation to work with this fiber is its large-scale offer, low cost and results already satisfactory in other studies, which are minutely prepared, treated and characterized. And to ensure no deterioration of these fibers made the use of ground ceramic waste, cement replacement part in the matrix, producing a paste free of free calcium hydroxide contributing to the protection of the fiber. Furthermore, to reduce water absorption and consequent reduction of the dimensional variation of the fiber, it is also used hornification treatment and sealing varnish base. In the production of this composite were used superplasticizer, medium sand, Portland cement (CP II 32-F) and water. With these plates were produced using acrylic formwork of 40x40x1cm. For the analysis of the mechanical properties, it was necessary to carry out tests of tensile stress, bending four points and three point bending. From the results, it can be concluded that the composite that showed the best results in terms of physical and mechanical characteristics was the one produced with hornificadas mallow fibers and coated with varnish and replacement of 30% of cement by ceramic waste, which showed elastic modulus 22.3 GPa, tensile strength of 23 MPa, and rupture modulus of 38.6 MPa.
Keywords: Resíduos cerâmicos
Termogravimetria
Placas cimentícias
Fibra de malva
???metadata.dc.subject.cnpq???: ENGENHARIAS: ENGENHARIA CIVIL
Language: por
???metadata.dc.publisher.country???: Brasil
Publisher: Universidade Federal do Amazonas
???metadata.dc.publisher.initials???: UFAM
???metadata.dc.publisher.department???: Faculdade de Tecnologia
???metadata.dc.publisher.program???: Programa de Pós-Graduação em Engenharia Civil
Citation: AGUIAR, Alcineia Silva de. Estudos das propriedades físicas e mecânicas de placas cimentícias reforçadas com fibras longas de malva. 2016. 109 f. Dissertação (Mestrado em Engenharia Civil) - Universidade Federal do Amazonas, Manaus, 2016.
???metadata.dc.rights???: Acesso Aberto
???metadata.dc.rights.uri???: http://creativecommons.org/licenses/by-nc-nd/4.0/
URI: http://tede.ufam.edu.br/handle/tede/5506
Issue Date: 23-Jun-2016
Appears in Collections:Mestrado em Engenharia Civil

Files in This Item:
File Description SizeFormat 
Dissertação - Alcineia S. Aguiar.pdf2.84 MBAdobe PDFThumbnail

Download/Open Preview


This item is licensed under a Creative Commons License Creative Commons