Título: Placas cimentícias obtidas a partir de argamassa de aluminossilicatos
Autor: Campos, Wellem Antônio Prestes 
Primeiro orientador: Vieira, Raimundo Kennedy
Resumo: As consequências negativas provocadas ao meio ambiente através da emissão de CO2, tem feito com que nos últimos anos pesquisas sejam desenvolvidas pela busca de novos materiais, dentre esses existem o metacaulim, usado como material pozolânico para produção de aluminossilicatos. Este trabalho objetivou obter uma argamassa de aluminossilicatos ativado por meio de solução alcalina, utilizando o metacaulim como material de substituição do cimento Portland. Para obtenção da placa de aluminossilicatos foi utilizada argila caulinitica retida na peneira ABNT 200 (0,074 mm) e calcinada na temperatura de 800 ºC durante 2 horas, sílica ativa e Hidróxido de sódio. Para obtenção da argamassa de cimento Portland foi utilizado o cimento CP IV-32 e como agregado miúdo uma areia lavada fina retida na peneira ABNT 200 (0,074 mm). A argila caulinitica e o metacaulim foram caracterizados através de ensaios químicos e mineralógicos, utilizando técnicas de fluorescência e difração de raio x, e através de ensaios físicos utilizando o frasco volumétrico “Le Chatelier e o permeabilímetro de Blaine. O desempenho mecânico dos corpos de prova cilíndricos foi obtido em ensaios de resistência à compressão simples, e o das placas de aluminossilicatos e cimento Portland foi obtido em ensaios de resistência à flexão em quatro pontos. Os resultados possibilitaram avaliar as características físico-químicas e mineralógica da matéria prima dos aluminossilicatos, possibilitaram também uma avaliação da resistência mecânica das placas, onde foi verificado que a placa de cimento Portland apresentou tensão máxima média à flexão superior de 5,3% em relação a da placa de aluminossilicatos.
Abstract: The negative effects caused to the environment by CO2 emissions has provoked, in the last years, the development of researchs for new materials, among these the metakaolin, used as pozzolanic material for production of aluminosilicate. This study aimed to get an aluminosilicate mortar activated by alkaline solution using metakaolin as replacement material for Portland cement. To obtain aluminosilicate board was used kaolinite clay retained in the sieve ABNT 200 (0.074 mm) and calcined at a temperature of 800° C for 2 hours, silica fume and sodium hydroxide. To obtain the Portland cement mortar was used CP IV-32 and as fine aggregate it was used washed sand retained at the sieve ABNT 200 (0.074 mm). The kaolinite clay and metakaolin were characterized by chemical and mineralogical assays using fluorescence techniques and x-ray diffraction, and through physical testing using the volumetric flask "Le Chatelier” and Blaine air permeability apparatus. The mechanical performance of the cylindrical specimens was obtained in strength tests to simple compression, and the aluminosilicate boards and Portland cement was obtained in flexural strength tests on four points. The results enabled to evaluate the physicochemical and mineralogical characteristics of the raw material of aluminosilicate and also allowed an evaluation of the mechanical resistance plates, where it was observed that Portland cement plate showed maximum average strain to the higher flexion of 5.3 % in relation of aluminosilicates of the plate.
Palavras-chave: Argila caulinitica
Aluminossilicatos
Metacaulim
Área(s) do CNPq: ENGENHARIAS: ENGENHARIA CIVIL
Idioma: por
País: Brasil
Instituição: Universidade Federal do Amazonas
Sigla da instituição: UFAM
Departamento: Faculdade de Tecnologia
Programa: Programa de Pós-graduação em Engenharia Civil
Citação: CAMPOS, Wellem Antônio Prestes. Placas cimentícias obtidas a partir de argamassa de aluminossilicatos. 2016. 54 f. Dissertação (Mestrado em Engenharia Civil) - Universidade Federal do Amazonas, Manaus, 2016.
Tipo de acesso: Acesso Aberto
URI: http://tede.ufam.edu.br/handle/tede/5395
Data de defesa: 11-Aug-2016
Appears in Collections:Mestrado em Engenharia Civil

Files in This Item:
File Description SizeFormat 
Dissertação - Wellem A. P. Campos.pdf1,43 MBAdobe PDFThumbnail

Download/Open Preview


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.