Título: Estudo das características física, mecânica e química de compósitos cimentícios reforçados com tecido de juta e malva tratado e adição de materiais pozolânicos
Autor: Vasconcelos, Daiana Góes 
Primeiro orientador: Vasconcelos, Raimundo Pereira de
Primeiro membro da banca: Melo Filho, João de Almeida
Segundo membro da banca: Marques, Maria Gorett dos
Terceiro membro da banca: Savastano Júnior, Holmer
Resumo: A presente pesquisa apresenta o desenvolvimento e caracterização de compósitos cimentícios reforçados com tecido das fibras de juta e malva. Para aumentar a durabilidade destes materiais foi utilizada uma matriz livre de hidróxido de cálcio, agente degradador de fibras naturais em ambiente cimentício. O tratamento do tecido foi realizado pelo processo de hornificação, visando reduzir a variação volumétrica das fibras e consequentemente melhorar a adesão fibra-matriz e a durabilidade. Placas cimentícias reforçadas com duas camadas de tecido de juta e malva foram produzidas com o auxílio de um sistema pneumático. A durabilidade dos compósitos foi investigada por meio do processo de envelhecimento acelerado (50 ciclos de molhagem e secagem) e os mesmos foram avaliados pelos ensaios de resistência à tração na flexão, análise microestrutural e caracterização física. Para a maioria das condições experimentais (placas reforçadas com tecido não tratado e com matriz de referência e modificada por 40% de metacaulinita), as placas compósitas apresentaram comportamento à tração na flexão com dupla fissuração aos vinte e oito dias de cura. Os compósitos reforçados com tecido tratado por 10 ciclos de hornificação apresentaram múltipla fissuração apenas no terço médio dos corpos de prova. Nos compósitos com metacaulinita, os tecidos hornificados e não tratados não resultaram em um aumento significativo na resistência à tração na flexão (MOR) em relação à matriz de referência reforçada (cerca de 6,5 MPa para todos os compósitos), contudo, aqueles apresentaram alta energia específica em relação a este (acréscimo acima de 100%). Após o envelhecimento, a matriz modificada e reforçada com tecido nas duas condições (não tratado e hornificado) foram eficientes, pois preservaram as características mecânicas, principalmente o MOR (6,5 MPa). Isto não foi observado para a matriz de referência reforçada, neste caso, houve perda de 25% na resistência (MOR = 5,15 MPa).
Abstract: The present research presents the development and characterization of cementitious composites reinforced with jute and malva fibers textile. In order to increase the durability of these materials, a free matrix of calcium hydroxide was used, a degrading agent of natural fibers in a cementitious environment. The treatment of the textile was performed by the hornification process, aiming to reduce the fiber volume variation and consequently to improve fiber-matrix adhesion and durability. Reinforced cementitious plates with two layers of jute and malva textile were produced by a pneumatic system and exhibited double-cracked flexural tensile behavior for most experimental conditions (plates reinforced with treated and untreated textile and matrix of reference and modified by 40% metakaolin) at twenty and eight days. The composites reinforced with textile treated for 10 cycles of hornification, presented multiple cracking only in the middle third of the specimens. The durability of the composites was investigated by means of the accelerated aging process (50 wetting and drying cycles) and they were evaluated by tensile strength tests, microstructural analysis and physical characterization. In the composites with metakaolin, the hornified and untreated textile did not result a significant increase in flexural tensile strength (MOR) in relation to the reinforced reference matrix (about 6.5 MPa for all composites), however, those presented high specific energy (more than 100% increase). After aging, the matrix modified and reinforced with textile in both conditions (untreated and hornified) were efficient, since they preserved the mechanical characteristics, mainly MOR (6.5 MPa). This was not observed for the reinforced reference matrix, in this case, there was a 25% loss in resistance (MOR = 5.15 MPa).
Palavras-chave: Matriz Cimentícia reforçada
Metacaulinita
Fibra de Juta - Durabilidade
Fibra de Malva - Durabilidade
Área(s) do CNPq: ENGENHARIAS: ENGENHARIA CIVIL
Idioma: por
País: Brasil
Instituição: Universidade Federal do Amazonas
Sigla da instituição: UFAM
Departamento: Faculdade de Tecnologia
Programa: Programa de Pós-graduação em Engenharia Civil
Citação: CAVALCANTE, Daiana Góes. Estudo das características física, mecânica e química de compósitos cimentícios reforçados com tecido de juta e malva tratado e adição de materiais pozolânicos. 2017. 123 f. Dissertação (Mestrado em Engenharia Civil) - Universidade Federal do Amazonas, Manaus, 2017.
Tipo de acesso: Acesso Embargado
Endereço da licença: http://creativecommons.org/licenses/by-nc-nd/4.0/
URI: https://tede.ufam.edu.br/handle/tede/6466
Data de defesa: 30-Oct-2017
Appears in Collections:Mestrado em Engenharia Civil

Files in This Item:
File Description SizeFormat 
Dissertação Parcial_Daiana Góes Cavalcante.pdf4,29 MBAdobe PDFThumbnail

Download/Open Preview


This item is licensed under a Creative Commons License Creative Commons