| ???jsp.display-item.social.title??? |
|
???item.export.label???
Please use this identifier to cite or link to this item:
https://tede.ufam.edu.br/handle/tede/6472| ???metadata.dc.type???: | Dissertação |
| Title: | Análise Estrutural da liga Half-Heusler TiNiSn por Mechanical Alloying |
| ???metadata.dc.creator???: | Gomes, Paola de Araújo  |
| ???metadata.dc.contributor.advisor1???: | Trichês, Daniela Menegon |
| ???metadata.dc.description.resumo???: | O estudo da liga Half-Heusler tem chamado muita atenção entres os pesquisadores devido as suas características e aplicações, de uma maneira geral, por caracterizarem-se como ligas ferromagnéticas, constituídas por elementos não magnéticos. Neste trabalho foi produzida e a liga TiNiSn, do tipo Half-Heusler, a fim de analisar sua estrutura. Nesta pesquisa, a liga TiNiSn foi produzida pela técnica de Moagem Mecânica de Alta Energia em dois tempos de moagem, a primeira em 3h com análise feita a cada uma hora, e a segunda em 4h sem pausas. A estrutura e seu comportamento térmico foram investigados pelas seguintes técnicas: Difração de raios X (DRX), Calorimetria Diferencial de Varredura (DSC), Tratamento Térmico (TT) e método de refinamento estrutural de Rietveld (MR). De acordo com os resultados obtidos, respectivamente, foi visto que a liga TiNiSn foi produzida em 4 h de moagem pelo método de mechanical alloying, seus difratogramas foram verificados afim de descobrir as fases formadas na liga sintetizada em 4 h, e pela análise de calorimetria diferencial de varredura (DSC) foi visto o comportamento térmico da amostra em temperaturas variadas, em uma faixa de 30 °C à 500 °C, subsequentemente, foi possível analisar a amostra pela técnica de tratamento térmico. |
| Abstract: | The study of the Half-Heusler alloy has drawn a lot of attention among the researchers due to their characteristics and applications, in general, to characterize as ferromagnetic alloys, constituted by non-magnetic elements. In this research, the TiNiSn alloy was produced by the Mechanical Alloyng in two routes, the first in 3h with analysis done at each hour, and the second at 4h straight. The structure and its thermal behavior were investigated by the following techniques: X-ray diffraction (XRD), Differential Scanning Calorimetry (DSC), Thermal Treatment (TT) and Rietveld refinement. According to results obtained, respectively, it was seen that the TiNiSn alloy was produced in 4h grinding by the mechanical alloying method, its diffractograms were verified in order to discover the phases formed in the synthesized alloy in 4h, and by the analysis of differential calorimetry of scanning was seen the thermal behavior of the sample at varied temperatures in a temperature range of 30 °C and 500 °C, so it was possible to analyze the sample by the Thermal Treatment technique. |
| Keywords: | Liga Half-Heusler Propriedades termoelétricas Mechanical Alloying Difração de raios x Half-Heusler Alloy X-ray Diffraction |
| ???metadata.dc.subject.cnpq???: | CIÊNCIAS EXATAS E DA TERRA: FÍSICA |
| Language: | por |
| ???metadata.dc.publisher.country???: | Brasil |
| Publisher: | Universidade Federal do Amazonas |
| ???metadata.dc.publisher.initials???: | UFAM |
| ???metadata.dc.publisher.department???: | Instituto de Ciências Exatas |
| ???metadata.dc.publisher.program???: | Programa de Pós-graduação em Física |
| Citation: | GOMES, Paola de Araújo. Análise Estrutural da liga Half-Heusler TiNiSn por Mechanical Alloying. 2018. 30 f. Dissertação (Mestrado em Física) - Universidade Federal do Amazonas, Manaus, 2018. |
| ???metadata.dc.rights???: | Acesso Aberto |
| ???metadata.dc.rights.uri???: | http://creativecommons.org/licenses/by-nc-nd/4.0/ |
| URI: | https://tede.ufam.edu.br/handle/tede/6472 |
| Issue Date: | 18-May-2018 |
| Appears in Collections: | Mestrado em Física |
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| Dissertação_Paola Gomes | 1.21 MB | Adobe PDF |  Download/Open Preview |
This item is licensed under a Creative Commons License