Title: | Desenvolvimento e caracterização física e mecânica de compósitos cimentícios reforçados com tecido têxtil de fibras de algodão |
Other Titles: | Development and physical and mechanical characterization of cementitious composites reinforced with cotton fiber textile fabric |
???metadata.dc.creator???: | Lima, Daniela Oliveira de |
???metadata.dc.contributor.advisor1???: | Melo Filho, João de Almeida |
???metadata.dc.contributor.referee1???: | Mendonça, Rannier Marques |
???metadata.dc.contributor.referee2???: | Vasconcelos, Raimundo Pereira de |
???metadata.dc.description.resumo???: | No presente estudo realizou-se o desenvolvimento e a caracterização de compósitos cimentícios reforçados com tecido têxtil de algodão. Os compósitos foram produzidos a partir de matriz cimentícia, constituída por cimento CP II E-32, metacaulinita, areia, água e superplastificante, traço 1:1:0,4. A matriz cimentícia foi dosada com substituição parcial de cimento Portland por 50% de metacaulinita com a finalidade de reduzir a quantidade de hidróxido de cálcio. O tecido foi caracterizado através de ensaios de absorção de água, difração de raios-X (DRX), termogravimetria (TG) e microscopia eletrônica de varredura (MEV). Os laminados cimentícios produzidos foram reforçados com tecido de algodão com frações volumétricas de 2, 3, 4 e 6%, sendo avaliados aos 28 dias por meio de ensaios físicos e mecânicos. Para a maioria das condições experimentais os compósitos apresentaram comportamento “strain hardening”, com formação de múltiplas fissuras, havendo incremento na resistência, deformação e tenacidade, à medida que foi aumentado o teor de fibra. O Compósito com teor de 6% de fibra resistiu a tensão máxima de ruptura de 7,26 MPa, apresentando em média 23 fissuras no terço médio da amostra, e cerca de 5,86 MPa com média de 57 de fissuras, submetidos a cargas de flexão e tração, respectivamente. Analisando os resultados, conclui-se que a fibra utilizada apresenta um potencial uso como reforço de laminados cimentícios, formando compósitos com boas propriedades físico-mecânicas. |
Abstract: | In the present study the development and characterization of cementitious composites reinforced with cotton textile fabric was carried out. The composites were produced from cementitious matrix, constituted by cement CP II E-32, metakaolin, sand, water and superplasticizer, trace 1: 1: 0.4. The cementitious matrix was made with partial Portland cement by 50% of metakaolin with the proposition to reduce the quantity of calcium hydroxide. The textile fabric was characterized by water absorption, X-ray diffraction (XRD), thermogravimetry (TG) and scanning electron microscopy (SEM) tests. The cementitious laminates produced were reinforced with cotton fabric with volumetric fractions of 2, 3, 4 and 6%, they were evaluated at 28 days by means of physical and mechanical tests. For most of the experimental conditions, the composites presented a “strain hardening” behavior, with formation of multiple cracking, with increase in the strength, deformation and tenacity, as the fiber content increased. The composite with a 6% fiber content presented the maximum tensile stress of 7.26 MPa, with on average 23 cracks in the middle third of the sample, and about 5.86 MPa with averge of 57 cracks, subjetcted to flexural and tensile loads, respectively. Analyzing the results, it was concluded that the fiber used presents a potential use as reinforcement of cementitious laminates, forming composites with good physico-mechanical properties. |
Keywords: | Materiais compostos Cimento Fibras têxteis Algodão |
???metadata.dc.subject.cnpq???: | ENGENHARIAS: ENGENHARIA CIVIL |
???metadata.dc.subject.user???: | Compósitos Metacaulinita Matriz cimentícia Tecido têxtil Fibra de algodão |
Language: | por |
???metadata.dc.publisher.country???: | Brasil |
Publisher: | Universidade Federal do Amazonas |
???metadata.dc.publisher.initials???: | UFAM |
???metadata.dc.publisher.department???: | Faculdade de Tecnologia |
???metadata.dc.publisher.program???: | Programa de Pós-graduação em Engenharia Civil |
Citation: | LIMA, Daniela Oliveira de. Desenvolvimento e caracterização física e mecânica de compósitos cimentícios reforçados com tecido têxtil de fibras de algodão. 2019. 107 f. Dissertação (Mestrado em Engenharia Civil) -Universidade Federal do Amazonas, Manaus, 2019. |
???metadata.dc.rights???: | Acesso Aberto |
???metadata.dc.rights.uri???: | http://creativecommons.org/licenses/by/4.0/ |
URI: | https://tede.ufam.edu.br/handle/tede/7303 |
Issue Date: | 18-Jul-2019 |
Appears in Collections: | Mestrado em Engenharia Civil |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
Dissertação_DanielaLima_PPGEC.pdf | 4.54 MB | Adobe PDF | Download/Open Preview |
This item is licensed under a Creative Commons License