Tipo do documento: Dissertação
Título: Síntese de Ortoniobatos de Samário (SmNbO4) polimórficos por moagem de alta energia
Autor: Brito Neto, Francisco Maciel de 
Primeiro orientador: Souza, Sérgio Michielon de
Primeiro coorientador: Paula, Marcos Marques da Silva
Segundo Coorientador: Santos, João Orestes Schneider
Primeiro membro da banca: Paula, Marcos Marques da Silva
Segundo membro da banca: Santos, João Orestes Schneider
Resumo: Amostras de óxido de samário (Sm2O3) e óxido de nióbio (Nb2O5) foram submetidas à técnica moagem mecânica de alta energia e sua evolução estrutural foi acompanhada por medidas de difração de raios X (DRX). Em poucas horas de moagem foram identificados cristais de SmNbO4 com dois polimorfismos, um monoclínico e outro tetragonal. Os difratogramas foram simulados por método de Rietveld e todos os parâmetros cristalográficos foram obtidos, assim como as respectivas quantidades de fases. Os tamanhos médios de cristalitos foram estimados pelo método da linha única (single-line) indicando que ambos polimorfos possuem dimensões nanométricas, ou seja, são nanoestruturados. Combinando medidas calorimétricas, tratamentos térmicos e difração de raios x a estabilidade estrutural das amostras foi estudada. Foi observado que a estrutura monoclínica sofre transição de fase para estrutura tetragonal em um processo exotérmico em torno de 850°C. A energia necessária para promover o processo foi obtida pelo método de Kissinger e as medidas de DRX indicam que a transição é irreversível.
Abstract: Samples of samarium oxide (Sm2O3) and niobium oxide (Nb2O5) were submitted to Mechanical alloying technique and their structural evolution was accompanied by x-ray diffraction (XRD) measurements. In a few hours of milling SmNbO4 crystals were identified with two polymorphisms, one monoclinic and the other tetragonal. The diffractograms were simulated by Rietveld method and all crystallographic parameters were obtained, as well as the respective amounts of phases. The average crystallite sizes were estimated by the single-line method, indicating that both polymorphs have nanosized dimensions, that is, they are nanostructured. Combining calorimetric measurements, thermal treatments and x-ray diffraction the structural stability of the samples was studied. It was observed that the monoclinic structure undergoes phase transition to tetragonal structure in an exothermic process around 850 °C. The energy needed to promote the process was obtained by the Kissinger method and the XRD measurements indicate that the transition is irreversible.
Palavras-chave: Terras Raras
Moagem de alta energia
Difração de Raios X
Método de Rietveld
Calorimetria Diferencial Exploratória
Rare Earths
Mechanical alloying
X-Ray Diffraction
Rietveld Method
Differential Scanning Calorimetry
Área(s) do CNPq: ENGENHARIAS: ENGENHARIA DE MATERIAIS E METALÚRGICA
Idioma: por
País: Brasil
Instituição: Universidade Federal do Amazonas
Sigla da instituição: UFAM
Departamento: Faculdade de Tecnologia
Programa: Programa de Pós-graduação em Ciência e Engenharia de Materiais
Citação: BRITO NETO, Francisco Maciel de. Síntese de Ortoniobatos de Samário (SmNbO4) polimórficos por moagem de alta energia. 2018. Dissertação. (Mestrado em Ciência e Engenharia de Materiais) - Universidade Federal do Amazonas, Manaus, 2018.
Tipo de acesso: Acesso Aberto
URI: https://tede.ufam.edu.br/handle/tede/6532
Data de defesa: 17-May-2018
Appears in Collections:Mestrado em Ciência e Engenharia de Materiais

Files in This Item:
File Description SizeFormat 
Dissertação_Francisco Brito Neto4,55 MBAdobe PDFThumbnail

Download/Open Preview


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.