Title: Caracterização mecânica à flexão em placas cimentícias reforçadas com tecidos de fibras de de Malva e Juta
???metadata.dc.creator???: Costa, Stefanny Di Samuel da Silva 
???metadata.dc.contributor.advisor1???: Andrade, Jean Carlos Silva
First advisor-co: Melo Filho, João de Almeida
???metadata.dc.contributor.referee1???: Macêdo Neto, José Costa de
???metadata.dc.contributor.referee2???: Ribas, Luciane Farias
???metadata.dc.description.resumo???: A utilização de fibras naturais como reforço em matrizes cimentícias é uma alternativa renovável e de baixo custo que gera compósitos com menor densidade e maior tenacidade. Dentre as diversas fibras produzidas no Brasil, podemos destacar as fibras de juta e malva, produzidas em larga escala no município de Manacapuru no Estado do Amazonas. Tais fibras tem grande potencial de aplicação em compósitos para a construção civil devido a suas propriedades mecânicas satisfatórias. Desta forma, este trabalho tem por objetivo analisar o desempenho de placas cimentícias reforçadas com fibras de juta e malva quanto ao número de camadas e o tipo de tratamento. Incialmente o caulim foi coletada no km 35 da BR 174, posteriormente foi calcinada a 700 ℃ por 2 horas. Em seguida a metacaulim produzida foi submetida a ensaios físico-químicos para sua caracterização e por fim foi adicionada na matriz cimentícia a fim de reduzir o hidróxido de cálcio (Ca(OH)2). Para determinação das suas propriedades físico-mecânicas a matriz cimentícia foi submetida a ensaios físico mecânicos e após isso, foram produzidas placas com substituição parcial do cimento Portland por metacaulim reforçadas com 3, 4 e 5 camadas de tecidos fibrosos tratados com 2 tipos de tratamentos que foram analisadas por seu comportamento a flexão. Por fim, a análise mecânica indicou que os compósitos moldados com 4 camadas de tecidos fibrosos e tratamento com resina acrílica apresentou tenacidade superior aos demais.
Abstract: The use of natural fibers as reinforcement in cementitious matrices is a renewable and lowcost alternative that generates composites with lower density and greater tenacity. Among the various fibers produced in Brazil, we can highlight the fibers of jute and mallow, produced on a large scale in the municipality of Manacapuru in the State of Amazonas and with great potential for application in composites for civil construction due to their satisfactory mechanical properties. Thus, this work refers to the bending mechanical analysis of cementitious slabs reinforced with jute and mallow fibers. Initially, kaolin was collected at km 35 of BR 174, later it was calcined at 700 ℃ for 2 hours. Afterwards, the metakaolin produced was submitted to physicochemical tests for its characterization and, finally, it was added to the cement matrix in order to reduce calcium hydroxide (Ca(OH)2). To determine its physical-mechanical properties, the cementitious matrix was subjected to tests. After optimizing the developed composite, plates were produced with partial replacement of Portland cement by metakaolin, reinforced with 3, 4 and 5 layers of fibrous fabrics treated with 2 types of treatments that were analyzed for their bending behavior. Finally, the mechanical analysis indicated that the composites molded with 4 layers of fibrous fabrics and treated with acrylic resin showed higher tenacity than the others.
Keywords: Fibras naturais
Fibra de Juta
Termogravimentria
Placas cimentícias
Fibras lignocelulósicas
???metadata.dc.subject.cnpq???: ENGENHARIAS
???metadata.dc.subject.user???: Compósitos Cimentícios
Metacaulim
Juta e Malva
Resistência à flexão
Language: por
???metadata.dc.publisher.country???: Brasil
Publisher: Universidade Federal do Amazonas
???metadata.dc.publisher.initials???: UFAM
???metadata.dc.publisher.department???: Faculdade de Tecnologia
???metadata.dc.publisher.program???: Programa de Pós-graduação em Ciência e Engenharia de Materiais
Citation: COSTA, Stefanny Di Samuel da Silva. Caracterização mecânica à flexão em placas cimentícias reforçadas com tecidos de fibras de de Malva e Juta. 2021. 94 f. Dissertação (Mestrado em Engenharia de Materiais) - Universidade Federal do Amazonas, Manaus, 2021.
???metadata.dc.rights???: Acesso Aberto
???metadata.dc.rights.uri???: http://creativecommons.org/licenses/by-nd/4.0/
URI: https://tede.ufam.edu.br/handle/tede/8510
Issue Date: 17-Aug-2021
Appears in Collections:Mestrado em Ciência e Engenharia de Materiais

Files in This Item:
File Description SizeFormat 
Dissertação_StefannyCosta_PPGCEM.pdfDissertação_StefannyCosta_PPGCEM3.33 MBAdobe PDFThumbnail

Download/Open Preview


This item is licensed under a Creative Commons License Creative Commons