???metadata.dc.type???: | Tese |
Title: | O efeito da adição do resíduo de madeiras folhosas processadas no desenvolvimento de placas de revestimento cerâmico |
Other Titles: | The effect of the addition of processed hardwood residue on the development of ceramic tiles |
???metadata.dc.creator???: | Costa, Germana de Vasconcelos Duarte |
???metadata.dc.contributor.advisor1???: | Sampaio, Paulo de Tarso Barbosa |
First advisor-co: | Ribeiro, Ruy Alexandre de Sá |
???metadata.dc.contributor.referee1???: | Melo, Maria da Gloria Goncalves de |
???metadata.dc.contributor.referee2???: | Nascimento, Claudete Catanhede |
???metadata.dc.contributor.referee3???: | Maia, Jair Max Furtunato |
???metadata.dc.contributor.referee4???: | Oliveira, Luiz Antonio de |
???metadata.dc.description.resumo???: | A Floresta Amazônica é uma região de grande biodiversidade e que necessita de um manejo sustentável de forma a permitir a conservação de seu bioma. É preciso utilizar seus recursos de forma racional e estimular atividades de sustentabilidade para criação de produtos inovadores, a exemplo dos de pó de serragem de madeiras tropicais, a fim de diminuir a incidência de descartes de resíduos sólidos na natureza de forma inadequada e desordenada, os quais geralmente causam danos, até mesmo irreversíveis, ao meio ambiente. Contudo, constata-se que não existem trabalhos sobre a incorporação do uso do pó de serragem de madeira tropical (in natura) em massas cerâmicas como substituto parcial da argila, para fabricação de placas de revestimentos de paredes para uso interno, foco neste trabalho. Diante de tais argumentações, levanta-se a seguinte questão de pesquisa: Qual o impacto do uso do pó de serragem de madeiras tropicais, gerado no processo produtivo de uma indústria madeireiro, quando misturado à argila, na produção de novos produtos cerâmicos de revestimento de parede, levando-se em consideração os valores sociais, ambientais e econômicos? Neste trabalho, portanto, tem-se como objetivo verificar a viabilidade de incorporar o pó de serragem das madeiras Pithecelobium racemosum Ducke (Angelim rajado) e Andira parviflora Ducke (Sucupira vermelha) em uma massa cerâmica composta como agentes porogênicos para fabricação de revestimentos cerâmicos, além de buscar minimizar os impactos destes no meio ambiente quando descartados. Os resíduos foram coletados na Indústria Mil Madeireira Preciosa Ltda, e a argila foi coletada no pátio da Cerâmica Montemar Indústria e Serviço de Coleta de Resíduos Ltda, localizadas, respectivamente, nos municípios de Itacoatiara e Iranduba no estado do Amazonas, Brasil. Para caracterização, foram desenvolvidas análises químicas, físicas e mineralógicas para avaliar o comportamento das matérias-primas e das formulações de massa entre a argila e a serragem, e as seguintes propriedades tecnológicas após a queima foram avaliadas: Retração Linear (RL), Resistência à Flexão (RF) de três pontos, Absorção de Água (AA), Porosidade (P) e Densidade Aparente (DA), Difratometria de Raio- X e Microscopia Eletrônica de Varredura (MEV) de acordo com as normas ABNT NBR 13818/1997 e ABNT NBR ISO 10545/2017. Em seguida, foram confeccionados 120 corpos de prova nas dimensões de 60x20x5 mm, sendo seis (6) amostras para cada grupo e com porcentagem específica. Após secagem, esses corpos de prova foram submetidos à sinterização, nas temperaturas de 750 °C e 850 °C, com taxa de aquecimento de 7 °C/min e tempo de queima de 180 min. A estimativa do RL, RF e AA foi obtida por meio de um modelo linear generalizado, de modo que os resultados foram validados por meio da Análise Estatística, utilizando métodos de análise descritiva, com cálculo das frequências e medidas de posição (médias e desvio padrão). Os resultados mostraram que a adição dos de pó de serragem, na argila, aumentou a densidade do solo seco, indicando um maior empacotamento. A retração linear de queima aumentou, com a inserção gradativa do teor de resíduo em todas as formulações em comparação com a argila pura, mas os resultados se mantiveram dentro dos parâmetros exigidos pela norma ABNT NBR 13818/1997 nas composições AR 2,5%, SV 2,5%, SV 5% e ARSV 10%, configurando um resultado satisfatório, pela importância do controle dimensional do produto. Embora tenha ocorrido diminuição da resistência mecânica nos corpos de prova, causada pelo tamanho da granulometria das partículas do pó de serragem, que foram superiores a 2μm, os resultados da absorção de água foram considerados significativos, após a inclusão do pó de serra de Andira parviflora Ducke (Sucupira vermelha), nas formulações SV 5% e SV 10%, quando sinterizadas na temperatura de 850 ºC. Conclui-se, com esses resultados, que o pó de serragem da Sucupira vermelha obteve melhor desempenho como agente porogênico em relação ao Angelim rajado, permitindo melhorias na argila vermelha de Iranduba/AM, deste modo, possui potencial para fabricação de produtos cerâmicos de base vermelha, tais como revestimentos porosos de classificação BIII. |
Abstract: | The Amazon Forest is a region of great biodiversity that needs sustainable management in order to allow the conservation of its biome. It is necessary to use its resources in a rational way and stimulate sustainability activities to create innovative products, such as the sawdust powders from tropical wood, in order to reduce the incidence of inadequate and disorderly disposal of solid residues in nature, which usually cause damage, even irreversible, to the environment. However, there are no studies on the incorporation of the use of sawdust powder from tropical wood (in natura) in ceramic masses as a partial substitute for clay, for the manufacture of wall coverings for internal use, the focus of this work. Faced with such arguments, the following research question arises: What is the impact of the use of the sawdust powders from tropical woods, generated in the production process of a wood industry, when mixed with clay, in the production of new ceramic products of wall covering, taking into account social, environmental and economic values? In this work, therefore, the objective is to verify the feasibility of incorporating sawdust powders from the wood Pithecelobium racemosum Ducke (Angelim rajado) and Andira parviflora Ducke (Sucupira vermelha) in a ceramic mass composed as porogenic agents for the manufacture of ceramic coatings, in addition to seeking to minimize their impacts on the environment when discarded. The residues were collected in Indústria Mil Madeireira Preciosa Ltda and the clay was collected in the yard of Cerâmica Montemar Indústria e Serviços de Coleta de Resíduos Ltda, located, respectively, in the municipalities of Itacoatiara and Iranduba in the state of Amazonas, Brazil. For characterization, chemical, physical and mineralogical analyzes were carried out to evaluate the behavior of raw materials and mass formulations between clay and sawdust, and the following technological properties after firing were evaluated: Linear Shrinkage (LS), Fracture Resistance (FR) of three-point, Water Absorption (WA), Porosity (P) and Apparent Density (AD), X-Ray Diffractometry and Scanning Electron Microscopy (SEM) according to ABNT NBR 13818/1997 and ABNT NBR ISO 10545/2017. Then, 120 specimens were made in the dimensions of 60x20x5 mm, with 6 samples for each group and with a specific percentage. After drying, these specimens were sintered at temperatures of 750 °C and 850 °C, with a heating rate of 7 °C/min and a burning time of 180 min. The estimation of LS, RF and WA was obtained through a generalized linear model, so that the results were validated through Statistical Analysis, using methods of descriptive analysis, with calculation of frequencies and position measurements (averages and standard deviation). The results showed that the addition of sawdust powders, in the clay, increased the density of the dry soil, indicating a greater packing. Linear firing shrinkage increased with the gradual insertion of residue content in all formulations compared to pure clay, but the results remained within the parameters required by ABNT NBR 13818/1997 in the compositions of AR 2.5%, SV 2.5%, SV 5% and ARSV 10%, configuring a satisfactory result, due to the importance of dimensional control of the product. Although there was a decrease in the mechanical strength of the specimens, caused by the size of the granulometry of the residues, which were greater than 2 μm, the water absorption obtained a significant result after the insertion of sawdust powders from Andira parviflora Ducke (Sucupira vermelha), in the formulations of MC5 (SV 2.5%) and MC6 (SV 5%), when sintered at a temperature of 850 ºC. It is concluded, with these results, that sawdust powders from Sucupira vermelha had better performance as a porogenic agent in relation to Angelim rajado, allowing improvements in the red clay from Iranduba/AM, in this way, it has potential for manufacturing red-based ceramic products, such as BIII-rated porous coatings. |
Keywords: | Redução de resíduos Resíduos vegetais |
???metadata.dc.subject.cnpq???: | CIENCIAS SOCIAIS APLICADAS |
???metadata.dc.subject.user???: | Pó de serragem Madeiras tropicais Massas cerâmica Revestimento poroso |
Language: | por |
???metadata.dc.publisher.country???: | Brasil |
Publisher: | Universidade Federal do Amazonas |
???metadata.dc.publisher.initials???: | UFAM |
???metadata.dc.publisher.department???: | Rede Bionorte |
???metadata.dc.publisher.program???: | Programa de Pós-graduação em Biodiversidade e Biotecnologia da Amazônia Legal - BIONORTE |
Citation: | COSTA, Germana de Vasconcelos Duarte. O efeito da adição do resíduo de madeiras folhosas processadas no desenvolvimento de placas de revestimento cerâmico. 2022. 144 f. Tese (Doutorado em Biodiversidade e Biotecnologia da Amazônia Legal) - Universidade Federal do Amazonas, Manaus (AM), 2022. |
???metadata.dc.rights???: | Acesso Aberto |
???metadata.dc.rights.uri???: | https://creativecommons.org/licenses/by-nc-nd/4.0/ |
URI: | https://tede.ufam.edu.br/handle/tede/9781 |
Issue Date: | 30-Aug-2022 |
Appears in Collections: | Doutorado BIONORTE |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
Tese_GermanaCosta_BIONORTE.pdf | 5.3 MB | Adobe PDF | Download/Open Preview |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.